Fabraic Aeir PVC 3200GSM
Fabraic Aeir PVC 3200GSM is a heavy-gauge coated textile engineered for inflatable air track construction, gymnastics training surfaces, and air tumble track assemblies. The base cloth is a high-tenacity polyester scrim with a 9x9 to 12x12 threads per inch weave, coated on both faces with plasticized polyvinyl chloride to a total fabric weight of 3200 g/m². The coating is applied through knife-over-roll or hot-melt calendering, followed by high-frequency or hot-air welding during fabrication. The fabric is supplied in rolls up to 2.0 m wide and is specified where drop-stitch or chambered air retention structures must withstand repeated dynamic loading from gymnasts, trampoline users, and parkour athletes.
Cén fáth a bhfuil 3200GSM Sonraithe le haghaidh Tógáil Aerrianta
Dáileadh Luchtaithe Faoi Thionchar Dinimiciúla
Soláthraíonn mais an bhrataithe 3200 g/m² neart teanntachta de 3,500 N/5cm go 4,500 N/5cm i dtreoracha dlúithe agus inneach, ag brath ar thógáil na scrim. Ligeann sé seo don fhabraic ualaí pointe ó thionchair tuirlingthe a dháileadh ar fud limistéar níos leithne den seomra aeir, ag laghdú an tiúchan struis ag seams sciath inmheánach agus línte táthaithe.
Puncture agus Friotaíocht Abrasion
Tá an tiús sciath ar Fabraic Aeir PVC 3200GSM idir 0.55 mm agus 0.70 mm in aghaidh an duine. Tugann tástáil scríobadh taber go ASTM D4060 luachanna meáchain caillteanais faoi bhun 0.30 g ag 1,000 timthriall le rothaí H-18, ag tacú le húsáid ar urlár giomnáisiam agus limistéir oiliúna lasmuigh ina dtarlaíonn teagmháil le dromchlaí scríobacha.
Coinneáil Aeir Trí Ionracas Weld
Cruthaíonn táthú ard-minicíochta an sciath PVC nasc móilíneach trasna an seam. Ag 3200 g/m², soláthraíonn mais an bhrataithe tiús ábhar leordhóthanach chun dul i bhfód le táthú gan dó tríd an scrim. Is gnách go sroicheann neart craiceann na seams táthaithe 80 N/5cm go 120 N/5cm, agus coinnítear caillteanas brú an tseomra faoi bhun 5% thar thréimhse 24 uair an chloig ag brú inmheánach 0.3 bar.
Cobhsaíocht Toiseach Faoi Bhrú
Tá an scrim poileistear i Fabraic Aer-Rianta PVC 3200GSM teas-socraithe roimh an sciath, rud a theorannú fadú go 3% go 5% ar ualach briste. Faoi thimthriallta boilscithe agus díbhoilscithe arís agus arís eile, coinníonn an fabraic céimseata aireagail gan stráice buan, rud a chaomhnaíonn na saintréithe preab atá beartaithe don aerrian thar a shaol seirbhíse.
Sonraí Tógála Fabraic
Sa chás go gcuirtear Fabraic 3200GSM i bhFeidhm
Ceisteanna Teicniúla ó Dhéantóirí agus ó Cheannaitheoirí
Cén modh táthú a mholtar chun fabraic 3200GSM a chomhcheangal?
Is é táthú tréleictreach ard-minicíochta an príomh-mhodh le haghaidh Fabraic Aeir PVC 3200GSM. Tacaíonn an tiús sciath le fuinneog táthú 0.5 go 2.5 soicind ag 27.12 MHz, ag brath ar chumraíocht leictreoid. Úsáidtear táthú aer-te le soic 40 mm ag 350 ° C go 400 ° C le haghaidh deisiúcháin pháirce agus céimseata casta nuair nach bhfuil uirlisiú HF ar fáil. Ba cheart go dtáirgfeadh an dá mhodh neart craiceann seam 80 N/5cm ar a laghad nuair a dhéantar tástáil air go ASTM D413.
Conas a fheidhmíonn an fabraic ag teochtaí ísle le linn stórála an gheimhridh?
Fabraic Aeir PVC 3200GSM remains flexible to -30°C when the plasticizer package is selected for cold-weather service. Standard formulations are rated to -20°C. For facilities that store inflated equipment in unheated spaces, specify the cold-flexible grade. Do not fold or crease the fabric below -10°C; allow the material to warm to 10°C or above before unrolling and inflating.
Cad is cúis le teip seam seomra agus conas a chuirtear cosc air?
Is gnách go n-eascraíonn teip seam i dtógáil rian aeir de bharr brú táthaithe neamhleor, dromchlaí brataithe éillithe, nó tiúchan struis ag acomhail sciath. A chinntiú go ndéantar dromchlaí brataithe a ghlanadh le halcól isopropil roimh tháthú, brú leictreoid a choinneáil laistigh den tsonraíocht trealaimh, agus pointí ceangail inmheánacha sciath a threisiú le dara pas táthú nó paiste den fabraic chéanna. Aithníonn tástáil brú gach seomra ag 1.5 uair an bhrú seirbhíse roimh an loingsiú seams lag sula sroicheann an táirge an t-úsáideoir deiridh.
An bhfuil fabraic 3200GSM oiriúnach do thógáil titim-stitch?
Fabraic Aeir PVC 3200GSM is used in drop-stitch panels where high chamber pressures above 0.5 bar are required. The fabric weight provides sufficient coating mass to anchor drop-stitch yarns without pull-through. For drop-stitch panels, the coating adhesion to the scrim is the critical property; specify a minimum of 100 N/5cm adhesion for drop-stitch applications to prevent yarn pull-out under pressure cycling.
Cén chaoi ar chóir an fabraic a ghlanadh agus a chothabháil idir séasúir?
Glan Fabraic Aeir PVC 3200GSM le tuaslagán glantach pH neodrach agus scuab bog nó éadach. Sruthlaigh le huisce glan agus lig dó tirim go hiomlán sula ndéantar é a dhíbhoilsciú agus a fhilleadh. Ná húsáid glantóirí tuaslagóir-bhunaithe, aicéatón, nó bleach clóirín, a bhaintear plaistigh as an sciath agus a luathaíonn scoilteadh dromchla. Stóráil trealamh díbhoilscithe i limistéar tirim, aeráilte ar shiúl ó sholas díreach na gréine agus rudaí géara.
Treoir maidir le Déantúsaíocht agus Stóráil
- Stóráil 3200GSM Rollaí Fabraic Aeir PVC go cothrománach ar raca croí-thacaithe i limistéar tirim ag 15 ° C go 30 ° C. Seachain rollaí cruachta níos mó ná dhá cheann ard chun cosc a chur ar chomhbhrú an sciath.
- Lig do na rollaí a bheith cothrom le teocht na ceardlainne ar feadh 24 uair an chloig ar a laghad roimh ghearradh nó táthú. Léiríonn fabraic fhuar solúbthacht laghdaithe an bhrataithe agus féadfaidh sé scoilteadh ag línte fillte le linn láimhseála.
- Gearr fabraic le lann rothlach géar nó scian te. Tá gearradh bás agus gearradh plotter inghlactha le haghaidh cruthanna painéil; imill ghearrtha a iniúchadh le haghaidh dílamination brataithe roimh tháthú.
- Coinnigh leictreoidí trealaimh táthú glan agus saor ó iarmhar PVC. Bíonn iarmhar carbónaithe ar leictreoidí ina chúis le dónna stua agus dromchla a chuireann isteach ar shláine seam.
- Tástáil-táthú sampla ó gach rolla roimh táthú táirgeachta. Is féidir le foirmiú sciath agus ábhar plasticizer athrú beagán idir baisceanna táirgeachta, agus d'fhéadfadh go mbeadh gá le paraiméadair táthú a choigeartú.