Scannán PETG Ardmharthanachta
Scannán PETG Ardmharthanachta is a thermoplastic polyester film based on polyethylene terephthalate glycol-modified resin. The glycol modification reduces the crystallization tendency of standard PET, producing an amorphous sheet with higher impact resistance and better thermoforming range. The film is supplied in thicknesses from 0.25 mm to 6.0 mm, in widths up to 2.1 m, with clear, colored, and frosted surface options. Impact strength reaches 8 to 12 kJ/m² by Charpy notched testing, and the film resists crazing under repeated flexural loading. High Durability PETG Film is specified for machine guards, signage, protective barriers, and thermoformed components where optical clarity and impact resistance are required together over a long service period.
Clár scannán saincheaptha
Scannán PETG Ardmharthanachta is supplied under an ODM/OEM arrangement. Thickness, width, surface finish, color, and cut format are set according to the buyer's drawing or performance brief. Clear and tinted grades, matte and anti-glare surfaces, and hard-coated variants are developed and documented against a single approved specification sheet, and the approved sheet governs every production lot.
Próifíl Feidhmíochta
Ionsú Tionchair Fuinnimh
Scannán PETG Ardmharthanachta absorbs impact energy through ductile deformation rather than brittle fracture. Charpy notched impact values of 8 to 12 kJ/m² are maintained at temperatures from -20°C to 40°C, so the film retains its protective function in outdoor and cold-storage installations where acrylic sheet cracks.
Friotaíocht Tuirse Solúbtha
Glactar le struchtúr éagruthach an scannáin lúbadh arís agus arís eile gan strus a chur faoi bhrú. Ní thugann tástáil tuirse flexural chuig ASTM D671 aon thionscnamh crack tar éis 100,000 timthriall ag aimplitiúid brú 0.5%, ag tacú le húsáid i ngardaí insí, daingneáin taispeána, agus painéil bhacainn sholúbtha.
Soiléireacht Optúil
Tarchuireann gráid shoiléire Scannán PETG Ardmharthanachta 84% go 90% den solas infheicthe le luachanna haise faoi bhun 1.0%. Níl an dromchla buí faoi soilsiú taobh istigh thar thréimhse 10 mbliana, agus coinníonn gráid chobhsaithe UV athrú datha laistigh de Delta E 2.0 faoi 2,000 uair an chloig de shíonchaitheamh luathaithe.
Friotaíocht Cheimiceach agus Glantacháin
Cuireann an scannán in aghaidh glantóirí caolaithe alcaileach, glantaigh neodracha, agus sláintitheoirí alcólbhunaithe. Tá teorainn le frithsheasmhacht in aghaidh tuaslagóirí aramatacha agus cetóin; déanann gníomhairí glantacháin atá bunaithe ar na ceimiceáin sin an snasta dromchla a bhaint agus a eisiamh ón bprótacal cothabhála.
Raon Teirmfhoirmithe
Scannán PETG Ardmharthanachta forms at 120°C to 160°C with a wide processing window. Deep draws and complex shapes are produced without pre-drying, and the formed part retains impact resistance at the stretched corners. Mold shrinkage is 0.2% to 0.6%, consistent across production runs.
Cobhsaíocht Toiseach
Coinníonn an scannán a thoisí gearrtha trasna athruithe taise ó 20% go 80% taiseachas coibhneasta. Tá leathnú líneach teirmeach 6.5 x 10⁻⁵ in aghaidh an °C, inchomparáide le alúmanam, a shimplíonn dearadh fráma áit a bhfuil an scannán suite idir easbhrúiteáin miotail.
Sonraí Teicniúla
Réimsí Feidhmchláir
Ceisteanna Ceannaitheora
Conas a dhéantar comparáid idir PETG agus aicrileach le haghaidh feidhmchláir tionchair?
Scannán PETG Ardmharthanachta provides higher impact resistance than cast acrylic at the same thickness, with Charpy notched values of 8 to 12 kJ/m² against typical acrylic values below 2 kJ/m². Acrylic offers higher surface hardness and better scratch resistance. For barrier and guard applications, PETG is specified; for high-scratch display faces, acrylic or a hard-coated PETG grade is preferred.
An bhfuil gá le triomú roimh theirmformáil?
Scannán PETG Ardmharthanachta does not require pre-drying in the normal shop environment. The film absorbs less than 0.2% moisture at 50% relative humidity, and that moisture level does not cause surface defects during forming. If the film has been stored in high humidity for an extended period, a 2-hour dry cycle at 65°C is recommended before forming thick-gauge sheet above 4.0 mm.
Cad iad na modhanna críochnú agus imeall atá oiriúnach?
Tá an scannán gearrtha ag ródaire CNC, léasair, chonaic, nó bás a ghearradh. Fágann gearradh léasair imeall snasta ach féadann sé tint ómra beag a tháirgeadh ag an líne gearrtha; Táirgeann ródú CNC le giotán aonfhliúit géar imeall glan. Baineann snasú imeall le lasair nó le cuimilt tuaslagóir marcanna an ródaire agus soiléiríonn sé an imeall le haghaidh feidhmeanna infheicthe.
Cén chaoi ar chóir an scannán a ghlanadh i seirbhís?
Glan le éadach bog agus le tuaslagán glantach neodrach nó le sláintitheoir alcólbhunaithe. Sruthlaigh le huisce glan agus tirim le éadach microfiber. Ná húsáid glantóirí gloine amóinia-bhunaithe, aicéatón, nó pillíní scríobach, a ionsaíonn an dromchla agus a laghdaíonn soiléireacht. Le haghaidh gráid atá brataithe le crua, lean treoracha cothabhála an tsoláthraí sciath.
An féidir an scannán a nascadh le hábhair eile?
Scannán PETG Ardmharthanachta bonds to rigid substrates with solvent-free PU adhesive, acrylic adhesive tape, or structural acrylic adhesive. Solvent-based adhesives containing ketones or aromatic solvents attack the film surface and cause crazing. Test coupon bonding should be completed before production, particularly where the assembly will be exposed to temperature cycling.
Nótaí Láimhseála agus Stórála
- Stóráil leatháin Scannán PETG Ardmharthanachta cothrom ar phailléid dochta i limistéar tirim ag 10°C go 30°C. Ná lean bileoga i gcoinne balla ar feadh tréimhsí fada; is féidir leis an mbileog Bow faoina mheáchan féin.
- Coinnigh an scannán cosanta i bhfeidhm le linn gearradh agus láimhseála chun scratches dromchla a chosc. Bain an chumhdach laistigh de 30 lá tar éis an tseachadta chun aistriú greamachán go dromchla an scannáin a sheachaint.
- Glan an scannán le éadach bog agus glantach neodrach. Déanann pillíní scríobacha, glantóirí amóinia-bhunaithe, agus táirgí tuaslagóir-bhunaithe ina bhfuil céatóin nó aramatacha damáiste don dromchla.
- Tacaigh leis an limistéar bileog iomlán le linn iompair agus suiteála. Is féidir le himill an leatháin thanaí nach dtacaítear leo sraonadh agus scoilt nuair a thógtar iad ag pointe amháin.
- Maidir le suiteálacha lasmuigh, sonraigh an grád UV-chobhsaithe agus deimhnigh go gceadaíonn an córas socraithe leathnú teirmeach 6.5 x 10⁻⁵ in aghaidh an °C gan srian a chur ar imeall an phainéil.